Light-curing of calcium hydroxide-based liners: pH analysis and calcium ion release / Fotoativação de forradores a base de hidróxido de cálcio: análise de pH e liberação de íons cálcio

Objective: Compare the pH values and calcium ion release of calcium hydroxide-based liner materials before and after light-curing. Material and Methods: The materials evaluated were: hydrox-cal white (HW), hydrox-cal dentin (HD), Biocal (BC) and UltraBlend Plus (UB). 120 samples of the liner materials were inserted into a PVC tube (n=15). The samples from HW+A, HD+A, BC+A and UB+A were subjected to photoactivation. The other groups HW+N, HD+N, BC+N and UB+N were only inserted in a glass tube with deionized water. The pH was measured 24 hours and 14 days after the inclusion of the samples with the aid of a pH meter. The calcium release was analyzed with the aid of an atomic absorption spectophotometer at 24h and 14 days. The results were submitted to the Shapiro-Wilk test, followed by ANOVA and Tukey test (p=0.05). Results: In 24h, the groups that were not light cured showed the highest pH values (p<0.05). In 14 days, BC+N and BC+A demonstrated the lowest pH values. The groups that were not light cured also showed higher calcium release values in 24h and 14 days (p<0.05). Conclusion: Photoactivation of calcium hydroxide-based liner materials negatively interferes with calcium ion release, as well as with pH.(AU)

Objetivo: Comparar os valores de pH e liberação de íons cálcio de materiais forradores à base de hidróxido de cálcio antes e depois da fotopolimerização. Material e métodos: Os materiais avaliados foram: Hidrox-cal branco (HW), Hidrox-cal dentina (HD), Biocal (BC) e UltraBlend Plus (UB). 120 amostras dos materiais de revestimento foram inseridas em um tubo de PVC (n=15). As amostras de HW +A, HD+A, BC+A e UB+A foram submetidas à fotoativação. Os demais grupos HW +N, HD+N, BC+N e UB+N foram inseridos apenas em um tubo de vidro com água deionizada. O pH foi medido 24 horas e 14 dias após a inclusão das amostras com o auxílio de um medidor de pH. A liberação de cálcio foi analisada com o auxílio de um espectrofotômetro de absorção atômica em 24h e 14 dias. Os resultados foram submetidos ao teste de Shapiro-Wilk, seguido de ANOVA e teste de Tukey (p=0,05). Resultados: Em 24h, os grupos não fotopolimerizados apresentaram os maiores valores de pH (p<0,05). Em 14 dias, BC+N e BC+A apresentaram os menores valores de pH. Os grupos não fotopolimerizados também apresentaram maiores valores de liberação de cálcio em 24h e 14 dias (p<0,05). Conclusão: A fotoativação de materiais de revestimento à base de hidróxido de cálcio interfere negativamente na liberação de íons cálcio e no pH (AU)

Impact of photoinitiator quality on chemical-mechanical properties of dental adhesives under different light intensities / Impacto da qualidade de fotoiniciadores nas propriedades químico mecânicas de adesivos dentais sob diferentes intensidades de luz

Objective: Evaluate the mechanical properties of experimental adhesive models with different photoinitiators (PI) polymerized by LED units of different power densities. Material and Methods: Three groups of adhesive models based on HEMA/BisGMA (45/55) were prepared in association with different PI combinations: G2 (control) ­ 2 PI: 0.5% CQ, 0.5% EDMAB; G3 - 3 PI: 0.5% CQ; 0.5% DMAEMA, 0.5% DPIHP; G4 - 4 PI: 0.5% CQ; 0.5% EDMAB; 0.5% DMAEMA; 0.5% DPIHP. The three formulations were polymerized at two different LED power densities: 550 mW/cm2 and 1200 mW/cm2. The degree of conversion (DC) of adhesive monomers was monitored in situ through the FTIR for 600 s. Specimens were prepared for each formulation for analysis mong adhesive systems (G2

Objetivo: Avaliar as propriedades mecânicas de modelos adesivos experimentais com diferentes fotoiniciadores (PI) polimerizados por unidades de LED de diferentes densidades de energia. Material e Métodos: Três grupos de modelos adesivos baseados em HEMA/BisGMA (45/55) foram preparados em associação com diferentes combinações de PI: G2 (controle) ­ 2 PI: 0,5% CQ, 0,5% EDMAB; G3 - 3PI: 0,5% CQ; 0,5% DMAEMA, 0,5% DPIHP; G4 - 4 PI: 0,5% CQ; 0,5% EDMAB; 0,5% DMAEMA; 0,5% DPIHP. As três formulações foram polimerizadas em duas densidades de potência de LED: 550 mW/cm2 e 1200 mW/cm2. O grau de conversão (DC) dos monômeros adesivos foi monitorado in situ através do FTIR durante 600 s. Amostras foram preparadas para cada formulação para análise de resistência à flexão (FS), módulo de elasticidade (ME), sorção (SOR) e solubilidade (SOL). Os dados foram submetidos aos testes ANOVA 2-fatores e Tukey (5%). Resultados: DC: houve diferença significativa entre os sistemas adesivos (G2

Color stability and degree of conversion of amine-free dual cured resin cement used with two different translucencies of lithium disilicate ceramics / Estabilidade de cor e grau de conversão de cimento resinoso dual sem amina usado com duas translucidezes diferentes de cerâmica de dissilicato de lítio

Objective: The present study aims to evaluate the color stability and degree of conversion of amine-free dual cured resin cement compared to light cured and amine-containing dual cured resin cements used with two different translucencies of thin esthetic restorations. Material and Methods: A total of 120 specimens were prepared for color stability testing (n=60). The specimens were divided into three main groups according to the resin cement type. Group 1: amine-free dual cured, Group 2: light cured, Group 3: amine-containing dual cured. Each group was further subdivided according to the ceramic translucency into two subgroups: high and low translucency. Color stability was assessed by a spectrophotometer before and after thermal aging. For the degree of conversion assessment (n=60), Fourier transform infrared spectroscopy was used at three different time intervals. Statistical analysis was performed using multi-factorial ANOVA, followed by one-way ANOVA with Bonferroni correction. Results: Amine-containing resin cement showed significantly higher ΔEab and ΔE00in both translucencies (4.5±0.3, 3.5±0.3 respectively for high translucency ceramic and 3.8±0.4, 3.0±0.3 respectively for low translucency) than the other tested cements (p<0.001). The highest degree of conversion (DC) was shown after 2 weeks by the amine-free dual cured resin cement (86.27±0.74). Conclusion: Amine-free dual cured resin cement can be an alternative to light cured one for cementation of thin veneers since it showed comparable color stability and high degree of conversion (AU)

Objetivo: O presente estudo tem como objetivo avaliar a estabilidade de cor e o grau de conversão do cimento resinoso dual sem amina em comparação com cimentos resinosos fotopolimerizáveis contendo amina usados com duas translucidezes diferentes em restaurações estéticas definitivas. Material e Métodos: Um total de 120 espécimes foram preparados para teste de estabilidade de cor (n=60). Os espécimes foram divididos em três grupos principais de acordo com o tipo de cimento resinoso. Grupo 1: polimerização dupla sem amina, Grupo 2: fotopolimerização, Grupo 3: polimerização dupla contendo amina. Cada grupo foi ainda subdividido de acordo com a translucidez da cerâmica em dois subgrupos: alta e baixa translucidez. A estabilidade da cor foi avaliada por um espectrofotômetro antes e após o envelhecimento térmico. Para a avaliação do grau de conversão (n=60), a espectroscopia de infravermelho com transformada de Fourier foi usada em três intervalos de tempo diferentes. A análise estatística foi realizada usando ANOVA multifatorial, seguida de ANOVA um faot com correção de Bonferroni. Resultados: O cimento resinoso contendo amina apresentou ΔEab e ΔE00 significativamente maiores em ambas as translucidezes (4,5±0,3, 3,5±0,3 respectivamente para cerâmica de alta translucidez e 3,8±0,4, 3,0±0,3 respectivamente para baixa translucidez) do que os outros cimentos testados (p< 0,001). O maior grau de conversão (DC) foi mostrado após 2 semanas pelo cimento resinoso dual sem amina (86,27±0,74). Conclusão: O cimento resinoso dual sem amina pode ser uma alternativa ao cimento polimerizável na restauração de facetas finas, uma vez que apresentou estabilidade de cor comparável e alto grau de conversão. (AU).

Influence of customization and light-curing device on the bond strength of glass fiber posts - in vitro study / Influência da reanatomização e do aparelho fotopolimerizador na resistência de união de pinos de fibra de vidro - estudo in vitro

Introduction: Endodontically treated teeth are usually affected by extensive structure loss requiring the use of intraradicular posts to provide retention and restoration. Objective: An in vitro assessment was performed on the bonding of glass fiber posts to the root dentin. Material and method: Ninety (n = 10) single bovine roots were used in a 3 x 3 x 3 factorial study with subdivided plots: post customization varying the presence and type of resin (without customization, conventional resin, and Bulk Fill resin), light-curing device (Valo, Radii-Cal, Rainbow), and root third (cervical, middle, and apical). Result: For the customization factor, Tukey's test (5%) showed the superiority of the Bulk Fill (8.16 MPa) and Z350 (7.40 MPa) groups compared to the control group (4.92 MPa), without differing from each other. All light-curing devices differed, showing the superiority of Valo (9.36 MPa), Radii (6.96 MPa) as an intermediate, and the inferiority of Rainbow (4.17 MPa). The cervical root third (7.81 MPa) was superior, the apical third was inferior (5.80 MPa), and the middle third (6.88 MPa) was an intermediate without differing from the others. Conclusion: The customization of glass fiber posts increases the bond strength to the root dentin, regardless of the resin used. There was a compromise in the apical third and when using light-curing devices with lower light intensity.

Introdução: Dentes com extensa perda de estrutura podem comprometer a retenção das restaurações ao remanescente dental, onde pinos intraradiculares são indicados. Objetivo: Avaliou-se in vitro a união de pinos de fibra de vidro à dentina radicular em função de diferentes modos de reanatomização, fotopolimerizadores e regionalização radicular. Material e método: Noventa (n=10) raízes bovinas uniradiculares foram usadas num estudo fatorial 3 x 3 x 3 com parcelas subdivididas: Reanatomização do pino, variando a presença e tipo de resina (Sem reanatomização, Resina Convencional e Resina Bulkfill); Fotopolimerizador (Valo, Radii-cal, Rainbow); e Terço radicular (cervical, médio e apical). Resultado: O teste de Tukey (5%) evidenciou para o Fator Reanatomização superioridade dos grupos BulkFill (8.16MPa) e Z350 (7.40MPa) ao grupo Controle (4.92MPa), sem diferirem entre si. Todos os fotopolimerizadores diferiram entre si, com superioridade de Valo (9.36MPa), Radii (6.96MPa) intermediário, e inferioridade de Raiwbow (4.17MPa). O terço radicular cervical (7.81MPa) foi superior e o apical inferior (5.80MPa), com o terço médio (6.88MPa) intermediário e sem diferir dos demais. Conclusão: Conclui-se que a reanatomização de pinos de fibra de vidro aumenta a resistência de união à dentina radicular, independentemente da resina utilizada, havendo prejuízo no terço apical e quando são empregados fotopolimerizadores com menor intensidade luminosa.

Can bulk-fill compromise the curing potential in deep cavities? / Bulkfill pode comprometer o potencial de polimerização em cavidades profundas?

Objective: To determine the effect of the restorative technique, material's opacity and the selected light sources on the curing potential (CP) in deep cavities. Material and Methods: The radiant exitance (mW/cm2) of two light curing units (Bluephase G2 and Radii-Cal) was determined at 0 and 8 mm distance from a power meter sensor (Ophir). Two bulk-fill composites of regular consistency (Opus, FGM; and Filtek One, 3M) and a conventional one (Sirius-Z, DFL) were considered and the level of their opacity were determined by a sphere-based spectrophotometer (SP60, X-Rite). The degree of C=C conversion (DC) was determined by spectroscopy (FTIR-ATR) at 0.05 and 8 mm depths and the CP considered the ratio between them. The "incremental technique" considered 4 increments of 2mm thickness each, whereas the "bulk-fill technique considered 2 increments of 4mm-thickness. Data were submitted to analysis of variance and Tukey's test (95%). Pearson's correlation tests were performed to calculate the possible relation between curing potential and materials' opacity. Results: With the incremental technique it was possible to achieve high CP regardless of the light source. The CP of bulk-fill composites was dependent on the light source, whereas Radii-Cal compromised the DC at 8 mm for both materials. The correlation between opacity and CP was dependent on the light source (r = 0.891707246 for Radii-Cal; r = 0.515703768 for Bluephase G2). Conclusion: The bulk-fill technique was dependent on the light source while the incremental was not. The influence of materials' opacity was dependent on the light curing unit.(AU)

Objetivo: Determinar o efeito da técnica restauradora, a opacidade do material e as fontes de luz selecionadas sobre o potencial de cura (PC) em cavidades profundas. Materiais e métodos: A saída radiante (mW/cm2) de duas unidades de cura por luz (Bluephase G2 e Radii-Cal) foi determinada a 0 e 8 mm de distância de um sensor de potência (Ophir). Dois compósistos bulkfill de consistência regular (Opus, FGM; e Filtek One, 3M) e um convencional (Sirius-Z, DFL) foram considerados e o nível de sua opacidade foi determinado por um espectrofotômetro (SP60, X-Rite). O grau de conversão C=C (DC) foi determinado por espectroscopia (FTIR-ATR) a 0,05 e 8 mm de profundidade e o PC considerou a relação entre eles. A técnica incremental considerou 4 incrementos de 2 mm de espessura cada, enquanto que a técnica bulkfill considerou 2 incrementos de 4 mm de espessura. Os dados foram submetidos à análise de variância e ao teste de Tukey (95%). Os testes de correlação de Pearson foram realizados para calcular a possível relação entre o potencial de cura e a opacidade dos materiais. Resultados: Com a técnica incremental foi possível obter um PC elevado, independentemente da fonte de luz. O PC de compósitos bulkfill foi dependente da fonte de luz, enquanto que Radii-Cal comprometeu o DC em 8 mm para ambos os materiais. A correlação entre opacidade e PC foi dependente da fonte de luz (r = 0,891707246 para Radii-Cal; r = 0,515703768 para Bluephase G2). Conclusão: O potencial de polimerização para a técnica bulkfill foi dependente da fonte de luz, enquanto para a técnica incremental não. A influência da opacidade dos materiais sobre a capacidade de polimerização foi dependente da unidade de fotoativação. (AU)

Effect of ceramic thicknesses and opacities on water sorption and solubility of a light-curing resin cement by different units

Aim: This study evaluated the water sorption and solubility of a light-cured resin cement, under four thicknesses and four opacities of a lithium disilicate ceramic, also considering three light-emitting diode (LED) units. Methods: A total of 288 specimens of a resin cement (AllCem Veneer Trans ­ FGM) were prepared, 96 samples were light-cured by each of the three light curing units (Valo ­ Ultradent / Radii-Cal ­ SDI / Bluephase II ­ Ivoclar Vivadent), divided into 16 experimental conditions, according to the opacities of the ceramic: High Opacity (HO), Medium Opacity (MO), Low Translucency (LT), High Translucency (HT), and thicknesses (0.3, 0.8, 1.5, and 2.0 mm) (n = 6). The specimens were weighed at three different times: Mass M1 (after making the specimens), M2 (after 7 days of storage in water), and M3 (after dissection cycle), for calculating water sorption and solubility. Results: The higher thickness of the ceramic (2.0 mm) significantly increased the values of water sorption (44.0± 4.0) and solubility (7.8±0.6), compared to lower thicknesses. Also, the ceramic of higher opacity (HO) generated the highest values of sorption and solubility when compared to the other opacities, regardless of the thickness tested (ANOVA-3 factors / Tukey's test, α = 0.05). There was no influence of light curing units. Conclusion: Higher thicknesses and opacities of the ceramic increased the water sorption and solubility of the tested light-cured resin cement

Microhardness homogeneity of RBCs light-cured with a multiple-peak LED and surface characterization after wear

Abstract This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.

Resumo Este estudo in vitro avaliou a homogeneidade do feixe de um fotopolimerizador de múltiplos picos na microdureza superficial e o efeito da escovação na microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho de compósitos a base de resina (RBCs) incrementais ou bulk-fill. Um fotopolimerizador LED (VALO) com quatro LEDs na ponteira (405, 445, 465A e 465B nm de pico de emissão) foi usado de acordo com o tempo recomendado por cada fabricante para obtenção de discos (n=10) de seis RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra e Filtek Bulk Fill. Os valores de microdureza foram obtidos seguindo o posicionamento de cada LED na superfície superior das amostras e foram analisados antes e após a escovação quanto a microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho. A microdureza foi considerada homogênea no topo da superfície, independentemente do tipo de RBCs ou comprimento de onda testados (p>0.05). No geral, a escovação não reduziu a microdureza das RBCs, mas influenciou o brilho para a maioria das RBCs (p<0.001). Charisma Classic apresentou os maiores valores de rugosidade superficial e perfil de rugosidade após a escovação (p<0.05). A perda de volume não diferiu entre as RBCs (p>0.05). Em conclusão, os diferentes comprimentos de onda do LED não alteraram a microdureza do topo da superfície, independentemente das RBCs testadas; e as resinas bulk-fill apresentaram alterações superficiais similares (microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e manutenção do brilho) quando comparadas às resinas convencionais após a escovação.

Effect of Light Sources on Bond Strength of Different Composite Resins Repaired with Bulk-Fill Composite / Efecto del tipo de fuente luz en la resistencia adhesiva de distintas resinas compuestas reparados con una resina bulk-fill

Abstract: The aim of this study was to evaluate and compare the effects of different light sources on shear bond strength when bulk-fill composite was used for the repair of different composite resins. A total of 126 samples made from six resin composites with different properties were aged (thermal-cycling with 5000 cycle), exposed to the same surface treatments and adhesive procedure. Then, they were repaired with a bulk-fill composite. At the polymerization step, each group was divided into three subgroups (n=7) and light cured with a QTH light source for 40s and two different LED light sources for 20s. Subsequently, the specimens were aged in distilled water at 37 ºC for 4 weeks and then subjected to shear bond strength test. Then, the specimens were examined under a stereomicroscope to identify modes of failure and visualized by Scanning Electron Microscope. Data obtained from the study were analyzed using ANOVA and Tukey HSD Test (α=0.05). In all groups, the light curing units had an impact on shear bond strength (p<0.05). Among the study groups, the greatest bond strength values were observed in the specimens repaired using the LED and the specimens repaired with the QTH light curing unit had the lowest bond strength values. It was concluded that the content of composite resins and light curing units may influence bond strength of different composites repaired with the bulk-fill composite.

Resumen: El objetivo de este estudio fue evaluar y comparar los efectos de diferentes fuentes de luz sobre la resistencia de la unión al cizallamiento cuando se utiliza una resina bulk-fill para la reparación de diferentes resinas compuestas. Se envejecieron un total de 126 muestras fabricadas con seis compuestos de resina con diferentes propiedades (ciclo térmico con 5000 ciclos), expuestas a los mismos tratamientos de superficie y procedimiento adhesivo. Luego, fueron reparadas con una resina bulk- fill. En el paso de polimerización, cada grupo fue dividido en tres subgrupos (n=7) y fotopolimerizado con una fuente de luz QTH por 40s y dos fuentes de luz LED por 20s. Posteriormente, los especímenes se envejecieron en agua destilada a 37 ºC durante 4 semanas y luego se sometieron a una prueba de resistencia adhesiva de cizalla. Luego, los especímenes fueron examinados bajo un estereomicroscopio para identificar los modos de falla y visualizados por el Microscopio Electrónico de Barrido. Los datos obtenidos del estudio fueron analizados usando el ANOVA y la prueba Tukey HSD (α=0.05). En todos los grupos, las unidades de fotopolimerización tuvieron un impacto en la fuerza de adhesión al cizallamiento (p<0,05). Entre los grupos de estudio, los mayores valores de fuerza de adhesión se observaron en los especímenes reparados utilizando el LED y los especímenes reparados con la unidad de fotopolimerización QTH tuvieron los valores de fuerza de adhesión más bajos. Se llegó a la conclusión de que el contenido de las resinas compuestas y las unidades de fotopolimerización pueden influir en la fuerza de adhesión de los diferentes compuestos reparados con resinas bulk-fill.

Physicochemical properties and biological effects of quaternary ammonium methacrylates in an experimental adhesive resin for bonding orthodontic brackets

Abstract Fixed orthodontic appliances may lead to biofilm accumulation around them that may increase caries risk. This study aimed to evaluate the influence of quaternary ammonium methacrylates (QAMs) on the physicochemical properties, cytotoxicity, and antibacterial activity of adhesive resins for orthodontic purposes. Methodology: A base resin was prepared with a comonomer blend and photoinitiator/co-initiator system. Two different QAMs were added to the base adhesive: dimethylaminododecyl methacrylate at 5 wt.% (DMADDM) or dimethylaminohexadecyl methacrylate (DMAHDM) at 10 wt.%. The base adhesive, without QAMs, (GC) and the commercial Transbond™ XT Primer 3M (GT) were used as control. The resins were tested immediately and after six months of aging in the water regarding the antibacterial activity and shear bond strength (SBS). The antibacterial activity was tested against Streptococcus mutans via metabolic activity assay (MTT test). The groups were also tested for the degree of conversion (DC) and cytotoxicity against keratinocytes. Results: The resins containing QAM showed antibacterial activity compared to the commercial material by immediately reducing the metabolic activity by about 60%. However, the antibacterial activity decreased after aging (p<0.05). None of the groups presented any differences for SBS (p>0.05) and DC (p>0.05). The incorporation of DMADDM and DMAHDM significantly reduced the keratinocyte viability compared to the GT and GC groups (p<0.05). Conclusion: Both adhesives with QAMs showed a significant reduction in bacterial metabolic activity, but this effect decreased after water aging. Lower cell viability was observed for the group with the longer alkyl chain-QAM, without significant differences for the bonding ability and degree of conversion. The addition of QAMs in adhesives may affect the keratinocytes viability, and the aging effects maybe decrease the bacterial activity of QAM-doped materials.

Polywave And Monowave Light-Curing Units Effects On Polymerization Efficiency Of Different Photoinitiators / Efeito Da Unidade De Cura Por Luz Polywave E Monowave Na Eficiência De Polimerização De Diferentes Fotoiniciadores

Objective: The objective of this study was to characterize and correlate the absorption spectra of three photoinitiators [camphorquinone (CQ), diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) and phenylbis (2,4,6-trimethylbenzoyl)-phosphine oxide (BAPO)], using second or third-generation light curing units (LCU), and to evaluate the degree of conversion and the physical properties of an experimental resin adhesive. Material and methods: Second-generation (Radii-cal® and Emitter D®) and third-generation (Valo® Cordless and Bluephase N®) LCU were assessed regarding spectrum and irradiance rate of emitted light. Also, the photoinitiators (CQ, TPO and BAPO) were characterized by a light absorption spectrum assessed by UV-Vis spectroscopy, degree of conversion and yellowing effect. Statistical analyzes considered two-way ANOVA and post-hoc Tukey test. Results: BAPO presented higher reactivity compared to TPO. Regarding degree of conversion of the photoinitiators activated by different light-curing units, the Emitter D® device promoted a high degree of conversion. BAPO presented the highest yellowing effect values. Conclusions: The emission and absorption characteristics of the photoinitiators were different. The polymerization reaction activated by the second-generation light-curing unit was reduced when using an experimental resin with photoinitiator TPO, and the third-generation light-curing unit showed a higher polymerization potential regardless of the photoinitiator. (AU)

Objetivo: Caracterizar e correlacionar os espectros de absorção de três fotoiniciadores [canforoquinona (CQ), difenil 2,4,6-trimetilbenzil óxido de fosfina (TPO) e óxido de di (2,4,6-trimetilbenzil) difenil fosfina (BAPO)], com unidades de fotoativação (LCU) de segunda ou terceira geração, e avaliar o grau de conversão e as propriedades físicas de um adesivo experimental. Material e métodos: LCU de segunda geração (Radii-cal® e Emitter D®) e terceira geração (Valo® Cordless e Bluephase N®) foram avaliadas quanto ao espectro e taxa de irradiância da luz emitida. Além disso, os fotoiniciadores (CQ, TPO e BAPO) foram caracterizados por um espectro de absorção de luz avaliado por espectroscopia UV-Vis, avaliado o grau de conversão dos adesivos e efeito de amarelamento. A análise estatística empregada foi ANOVA duas vias e teste post-hoc de Tukey. Resultados: BAPO apresentou maior reatividade comparado ao TPO. Em relação ao grau de conversão dos fotoiniciadores ativados por diferentes aparelhos fotopolimerizadores, o dispositivo Emitter D® promoveu um alto grau de conversão. BAPO apresentou os maiores valores de efeito de amarelamento. Conclusões: As características de emissão e absorção dos fotoiniciadores foram diferentes. A reação de polimerização ativada pelas unidades de fotopolimerização de segunda geração foi reduzida com o uso de uma resina experimental com fotoiniciador TPO. As unidades de fotopolimerização de terceira geração apresentaram maior potencial de polimerização independentemente do fotoiniciador. (AU)

Effect of Light Curing Modes on the Color Stability of a Nanohybrid Composite Immersed in Different Beverages / Efecto de diferentes modos de fotopolimerización en la estabilidad del color de una resina compuesta nanohíbrida inmersa en diferentes bebidas

Abstract: Aim: Sufficient polymerization remains as crucial for composites to prevent discoloration. Both LEDs and halogen units are used for polymerization and different curing modes are improved to overcome inadequate polymerization. This in vitro study investigated staining susceptibility of a nano-hybrid resin composite light-cured in different modes and immersed in different staining media. Methods: Disc-shaped specimens were prepared from nano-hybrid resin composite (Filtek Z550) and light- cured according to following modes: Halojen (GI), LED standard (GII), LED pulse (GIII) or LED ramp (GIV). Half of the specimens of each group (n=7) were stored in one of the staining media (red wine or coffee) for 10 min/day during experimental period. Measurements were performed using spectrophotometer according to CIEL*a*b system at baseline and on 7, 28 and 56 days. Colour differences (∆E) between groups were submitted to statistical analysis. Results: Regarding 7-day evaluation, colour change values of specimens immersed in coffee revealed no remarkable difference among curing modes (p>0.05); whereas specimens in GIV were significantly less stained compared to specimens in GII and GIII when immersed in red wine. Regarding 56- days of evaluation, specimens of GIV showed statistically significant colour change in red wine compared to other groups. However specimens in GI revealed the least staining after 56-days of coffee immersion, and this result was statistically different from LED groups. Conclusion: This study suggest that light-curing mode influences the staining susceptibility of the tested composite. Composites polymerized with halogen unit showed lower staining than all LED modes. Despite novel light sources, halogen units may still used reliably at clinics.

Resumen: Objetivo: La polimerización suficiente sigue siendo crucial para que los compuestos eviten la decoloración. Tanto los LED como las unidades halógenas se utilizan para la polimerización y se mejoran los diferentes modos de curado para superar la polimerización inadecuada. Este estudio in vitro investigó la susceptibilidad a la tinción de un compuesto de resina nano-híbrida curado a la luz en diferentes modos y se sumergió en diferentes medios de tinción. Métodos: Las muestras en forma de disco se prepararon a partir de un compuesto de resina nano-híbrida (Filtek Z550) y se curaron con luz de acuerdo con los siguientes modos: Halojen (GI), estándar de LED (GII), pulso de LED (GIII) o rampa de LED (GIV). La mitad de las muestras de cada grupo (n = 7) se almacenaron en uno de los medios de tinción (vino tinto o café) durante 10 minutos / día durante el período experimental. Las mediciones se realizaron utilizando un espectrofotómetro de acuerdo con el sistema CIEL * a * b en la línea de base y en 7, 28 y 56 días. Las diferencias de color (∆E) entre los grupos se sometieron a análisis estadístico. Resultados: Con respecto a la evaluación de 7 días, los valores de cambio de color de las muestras sumergidas en café no revelaron diferencias notables entre los modos de curado (p> 0.05); mientras que las muestras en GIV se tiñeron significativamente menos en comparación con las muestras en GII y GIII cuando se sumergieron en vino tinto. Con respecto a los 56 días de evaluación, las muestras de GIV mostraron un cambio de color estadísticamente significativo en el vino tinto en comparación con otros grupos. Sin embargo, las muestras en GI revelaron la menor tinción después de 56 días de inmersión en el café, y este resultado fue estadísticamente diferente de los grupos LED. Conclusión: este estudio sugiere que el modo de fotopolimerización influye en la susceptibilidad de tinción del material compuesto probado. Los compuestos polimerizados con una unidad halógena mostraron una tinción más baja que todos los modos LED. A pesar de las nuevas fuentes de luz, las unidades halógenas todavía pueden usarse de manera confiable en las clínicas.

Effects of curing modes on depth of cure and microtensile bond strength of bulk fill composites to dentin

Abstract Objectives To compare the microtensile bond strength (µTBS) and depth of cure (DOC) of bulk-fill composites cured by monowave (MW) and polywave (PW) LED units using different curing times. Methodology Three composites were tested: Tetric EvoCeram Bulk Fill (TBF), Filtek Bulk Fill (FBF), and Tetric EvoCeram (T; control). Flat dentin surfaces treated with adhesive (AdheSE Universal®, Ivoclar Vivadent) were bonded with 4 mm cylindrical samples of each bulk-fill composite material (n=6) and cured with monowave (Satelec) or polywave (Bluephase Style) curing units for 10 or 20 seconds. After 24 hours, teeth were sectioned into individual 0.9 mm2 beams and tested for µTBS. Failure modes were analysed. Moreover, the DOC scrape test (IOS 4090) was completed (n=5) following the same curing protocols. Two-way ANOVA (a=0.05) was performed, isolating light-curing units. Results For samples cured with the MW light-curing unit, no significant effects were observed in the µTBS results between any of the resin composite brands and the curing times. Conversely, when resins were cured with a PW light unit, a significant effect was observed for TBF resin. In general, bulk-fill composites presented greater DOC and longer curing time resulted in higher DOC for all composites. Conclusion The µTBS of the composites to dentin was not affected by the curing mode of the resins, except for TBF cured with PW light unit. Bulk-fill composites exhibit greater DOC than conventional resin-based composites.

Interfacial properties and bottom/top hardness ratio produced by bulk fill composites in dentin cavities

Abstract The aim of this study was to evaluate the bond strength, bottom/top hardness ratio, marginal adaptation, and interfacial nanoleakage of regular viscosity bulk fill composites (RVBFC) and regular viscosity traditional composites (RVTC). Two RVBFC (Filtek Bulk Fill and Aura Bulk Fill) and two RVTC (Filtek Z250XT and Aura) were assessed. Forty conical cavities (4.8×2.8×4.0) were prepared in bovine dentin and restored with composites (n=10). After 24h in water, marginal adaptation was evaluated by staining with a caries detector. The top and bottom surfaces of the conical restorations were stained for five seconds and the gap percentage in the composite/dentin interface was determined using digital images on a measurement program (ImageTool). The Vickers microhardness was measured and the bottom/top microhardness ratio (B/T) was determined. Push-out bond strength test was performed in a universal testing machine (0.5mm/min) and failure modes were evaluated in a stereomicroscope (20×). Other specimens (n=3) were produced for interfacial nanoleakage evaluation. Data were analyzed using one and two-way ANOVA and Tukey's test (α=0.05). The gap percentage was higher in the bottom compared to the top. The B/T ratio of the Aura Bulk Fill was statistically lower than other composites. Push-out bond strength were similar among composites. The RVBFC presented lower nanoleakage than the RVTC in the bottom of the conical restoration and there was no difference among the materials in the top surfaces. In conclusion, Filtek Bulk Fill performed better than Aura Bulk Fill regarding the analyzed properties.

Resumo O objetivo deste estudo foi avaliar a resistência de união, razão base/topo de microdureza, adaptação marginal e nanoinfiltração interfacial de resinas compostas bulk fill (BF) e tradicional (RT) de viscosidade regular.: Duas BF (Filtek Bulk Fill e Aura Bulk Fill) e duas RT (Filtek Z250XT e Aura) foram testados. Quarenta cavidades cônicas (4,8×2,8×4,0) foram preparadas em dentina bovina e restauradas com os compósitos (n=10). Depois de 24 h em água, a adaptação marginal foi avaliada por meio do corante com detector de cárie. As faces de topo e base das restaurações cônicas foram coradas por cinco segundos e a porcentagem de fendas na interface compósito/dentina foi determinada utilizando-se imagens analisadas num programa (ImageTool). A microdureza Vickers foi mensurada e a razção base/topo de microdureza (B/T) foi determinada. A resistência de união por push-out foi executada numa máquina de ensaios universal (0,5mm/min) e o padrão de fratura avaliado num estereomicroscópio (20x). Espécimes adicionais (n=3) foram confeccionados para avaliação da nanoinfiltração interfacial. Os dados foram analisados por meio de ANOVA a dois fatores e teste de Tukey (a=0,05). A porcentagem de fendas foi maior na base que no topo. A B/T da Aura Bulk Fill foi estatisticamente menor que os demais compósitos. A resistência de união por push-out foi similar entre os compósitos. As BF apresentaram menos nanoinfiltração que as RT na base das restaurações cônicas e não houve diferenças entre os materiais no topo. Conclui-se que a Filtek Bulk Fill comportou-se melhor que a Aura Bulk Fill considerando-se as propriedades analisadas.

Ultimate tensile strength of total and self-etch adhesives: effect of light irradiation distance

Objective: To evaluate the ultimate tensile strength (UTS) of total and self- etch adhesives irradiated at different distances. Materials and Methods: Sixty cylindrical specimens of 0.78mm diameter and 10 mm length were prepared of two types of adhesive systems total etch Excite DSC (EX ­ Ivoclar Vivadent, Schaan, Liechtenstein) and one-step self-etch Clearfil S3 Bond (S3, Kuraray Medical Inc., Tokyo, Japan). Specimens of each adhesive were divided into three groups according to the light irradiation distance (0, 2, 4mm) (n=10). Each specimen was attached to universal testing machine (Digital Force Gauge, IMADA CO., LTD, Japan) and loaded at cross head speed of 1mm/min until failure. Data were analyzed using two-way ANOVA and Independent Student t-test at p< 0.05. Results: Mean UTS for total etch (24.63, 18.19, 17.26 Mpa) and for self-etch (12.68, 8.53, 7.58Mpa) at (0, 2, 4mm) distances. Specimens irradiated directly show significantly the highest UTS while those irradiated at 4mm show the lowest values (p<0.05). Excite DSC total etch adhesive have higher UTS than Clearfil S3 self-etch adhesive regardless of irradiation distance (p<0.05).Conclusions: The UTS of the evaluated adhesives was light irradiation distance and adhesive system dependant.

Effect Of Preheating On Surface Roughness And Microhardness Of A Nanohybrid Composite Resin - An In Vitro Study

Introduction: The success of dental composites in restorative dentistry stems from their good aesthetic properties andadequate durability. The clinical performance of composite resins is directly related to the degree of monomer conversion afterphoto polymerization. Placing composites at an elevated temperature reduce their viscosity and increase the efficiency ofpolymerization. Heating the composite prior to placement in the cavity increases monomer conversion rate and therefore theduration of the irradiation period may be reduced.Purpose of Study: Evaluate and compare effect of pre-heating on surface roughness and microhardness of nanohybrid compositeresin subjected to two different temperatures and two different durations using light emitting diode curing unit (LED LCU).Methods: Nanohybrid composite resin was tested at two temperatures (37°C and 55°C) and pre-heating of composite wasdone using incubator at two durations (10 and 20 minutes) respectively. Samples were injected into cylindrical Teflon molds andthe top surface of the specimens were polymerized using LED LCU for 40 s. After preservation for 24 h, specimens checkedfor surface roughness and Vickers hardness measurements. Statistical analysis were performed using one-way analysis ofvariance and Tukey post hoc test at a level of significance of P < 0.05 for both surface roughness and microhardness.Results: Pre-heating of composite affect on microhardness and did not influence on surface roughness.Conclusion: Pre-heating of resin composite increases microhardness and no significant effect on roughness.

Bond strength and marginal microleakage in restorations photopolymerized with LED and halogen light associated with three application modes of a universal adhesive system: in vitro study / Resistência de união e da microinfiltração marginal em restaurações fotopolimerizadas com LED e luz halógena associadas a três modos de aplicação de um sistema adesivo universal: estudo in vitro

ABSTRACT Objective: This study aimed to assess the bond strength and marginal microleakage in composite resin restorations, using the Single Bond Universal adhesive system associated with Ultralux (halogen) and Bluephase (LED) light curing units. Methods: For bond strength, 80 healthy human third molars were divided into halogen light (n=40) and LED (n=40), and subdivided according to the following application techniques for the adhesive system: etch-and-rinse (enamel), self-etching (enamel), etch-and-rinse (dentin), and self-etching (dentin). The teeth were subjected to the microtensile test and the fracture pattern was observed under an optical microscope at 40X magnification; they were analyzed by ANOVA, and Fisher and Tukey's tests (5%). For the marginal microleakage test, 120 class II cavities were prepared in 60 healthy human third molars that were randomly divided into halogen light (n=30) and LED (n=30), and subdivided according to the following application techniques for the adhesive system: etch-and-rinse, selective etching, and self-etching. The teeth were thermocycled 2000 times (±5/55°C), stained in 5% basic fuchsin and sectioned for qualitative and quantitative assessments; they were analyzed by Kruskall-Wallis and Dunn tests (5%). Results: For the bond strength of enamel and dentin, the adhesive application with prior acid etching was better than self-etching (p<0.0001), regardless of the type of light curing unit (p<0.05). Etch-and-rinse showed the lowest microleakage values (p<0.0001). Conclusion: Etch-and-rinse obtained the best results relative to the other application techniques for the adhesive system in both tests, regardless of the type of light curing unit.

RESUMO Objetivo: Avaliar a resistência de união e microinfiltração marginal em restaurações de resina composta, utilizando sistema adesivo Single Bond Universal associado com fotoativadores Ultralux (halógeno) e Bluephase (LED). Métodos: Para resistência de união, oitenta terceiros molares humanos hígidos foram divididos: Halógena (n=40); LED (n=40), sendo subdivididos de acordo com a técnica de aplicação do sistema adesivo: condicionamento total-esmalte; autocondicionante-esmalte; condicionamento total-dentina; autocondicionante-dentina. Os dentes foram submetidos ao teste de microtração e o padrão de fratura foi observado em microscópio ótico - 40X de aumento, analisadas pelos testes ANOVA, Tukey e Fisher (5%). Para o ensaio de microinfiltração marginal, 120 cavidades classe II foram preparadas em sessenta terceiros molares humanos hígidos, aleatoriamente divididos: Halógena (n=30); LED (n=30) e subdivididos de acordo com a técnica de aplicação do sistema adesivo: condicionamento total; condicionamento seletivo; autocondicionante. Os dentes foram termociclados 2000 vezes (±5/55ºC), corados em fucsina básica 5% e seccionados para avaliações qualitativa e quantitativa, analisados pelos testes Kruskall-Wallis e Dunn (5%). Resultados: Para resistência de união em esmalte e dentina, a aplicação do adesivo com condicionamento ácido prévio, foi melhor que o autocondicionante (p<0.0001), independentemente do tipo de fotoativador utilizado (p<0.05). O condicionamento total mostrou os menores valores de microinfiltração, (p<0.0001). Conclusão: O condicionamento total, obteve os melhores resultados em relação às outras técnicas de aplicação do sistema adesivo em ambos os testes, independentemente do tipo de aparelho fotoativador.

Financial estimate of light-curing composite resin treatment after National Health Insurance Service coverage / 대한구강보건학회지

OBJECTIVES: This study aimed to estimate the financial budget of light-curing composite resin fillings based on the expanded coverage of the National Health Insurance Service (NHIS), called “Moon Care.” METHODS: The estimated population with dental caries and the amount of light-curing composite resins used were determined. The fees for the resin fillings per tooth were considered for the calculations. The expected budget for the next five years for children and adolescents aged 5–12 and 5–19 years were calculated. RESULTS: During the first year of the coverage, the budget for children and adolescents aged <19 years was estimated to be 201.8 billion South Korean won (5–9 years, 17.9 billion South Korean won; 10–14 years, 76.6 billion South Korean won; and 15–19 years, 107.3 billion South Korean won). The total budget for the next five years for children and adolescents aged <19 years was estimated at 946.4 billion South Korean won. Likewise, the budget for children aged <12 years during the first year of the coverage was estimated at 63.9 billion South Korean won (5–9 years, 17.9 billion South Korean won and 10–12 years, 46 billion South Korean won), and the total budget for the next five years was estimated at 315.9 billion South Korean won. CONCLUSIONS: Government healthcare plans should be established based on treatment needs and financial estimations. All the items in the NHIS, including the light-curing composite resin filling, should be considered based on their contribution to oral health promotion. Furthermore, in the long term, the coverage for preventive health services should be included in the health insurance.

Inflammatory Effect of Light-Emitting Diodes Curing Light Irradiation on Raw264.7 Macrophage / 치위생과학회지

BACKGROUND: The light-emitting diode (LED) curing light used is presumed to be safe. However, the scientific basis for this is unclear, and the safety of LED curing light is still controversial. The purpose of this study was to investigate the effect of LED curing light irradiation according to the conditions applied for the polymerization of composite resins in dental clinic on the cell viability and inflammatory response in Raw264.7 macrophages and to confirm the stability of LED curing light. METHODS: Cell viability and cell morphology of Raw264.7 macrophages treated with 100 ng/ml of lipopolysaccharide (LPS) or/and LED curing light with a wavelength of 440~490 nm for 20 seconds were confirmed by methylthiazolydiphenyl-tetrazolium bromide assay and microscopic observation. The production of nitric oxide (NO) and prostaglandin E2 (PGE2) was confirmed by NO assay and PGE2 enzyme-linked immunosorbent assay kit. Expression of interleukin (IL)-1β and tumor necrosis factor (TNF)-α in total RNA and protein was confirmed by reverse transcription polymerase chain reaction and Western blot analysis. RESULTS: The LED curing light did not affect the viability and morphology of normal Raw264.7 cells but affected the cell viability and induced cytotoxicity in the inflammation-induced Raw264.7 cells by LPS. The irradiation of the LED curing light did not progress to the inflammatory state in the inflammation-induced Raw264.7 macrophage. However, LED curing light irradiation in normal Raw264.7 cells induced an increase in NO and PGE2 production and mRNA and protein expression of IL-1β and TNF-α, indicating that it is possible to induce the inflammatory state. CONCLUSION: The irradiation of LED curing light in RAW264.7 macrophage may induce an excessive inflammatory reaction and damage oral tissues. Therefore, it is necessary to limit the long-term irradiation which is inappropriate when applying LED curing light in a dental clinic.

Influence of light-curing on the translucence change and color stability of amine-free dual-cured resin cements / 대한치과재료학회지

The aim of this study was to investigate the influence of light-curing on the translucency change and color-stability of amine(tertiary)-free dual-cured resin cements after accelerated aging. Two curing modes (dual-curing and self-curing) were applied on three dual-cured resin cements (Duo-Link Universal [DLU], Nexus Third Generation [NX3] and RelyX Ultimate [RXU]) in this study. Ten specimens were fabricated for each group. In dual-cured groups only, light-activation was performed with polywave-LED curing unit (Bluphase, Ivoclar Vivadent, Schaan, Liechtenstein), where each sides of the samples were photo-polymerized for 60 seconds. Self-cured groups were kept in the dark storage for 24 hours. The color of the specimens was measured with spectrocolorimeter (NF999, Nippon Denshoku, Japan) after 24 hours of making samples. After the initial color measurements, the specimens were subjected to accelerated aging procedure. Spectrophotometric analysis was carried out on day 7, day 14, day 21 and day 28 of accelerated aging in 60 ℃ of distilled water. The color characteristics, color difference (ΔE*), and translucency parameter (TP) of specimens were calculated according to the CIE L*a*b* color system before and after aging. All the ΔE* values and TP values were analyzed by 2-way analysis of variance. After aging, all groups revealed clinically perceptible color differences (ΔE*>3.3). Differences in ΔE* values of self-cured groups were significantly higher than those of dual-cured groups in NX3 and RXU. But there were no significant differences in ΔE* between dual-cured mode and self-cured mode of DLU. All mean b* values increased after aging. All mean L* values decreased after aging except for self-cured RXU cement. TP values also decreased with aging. TP values of self-cured groups were significantly lower than those of dual-cured groups in NX3 and RXU. Hence, in conclusion, despite the absence of tertiary amine in the dual-cured resin cements, such resin cements should be polymerized with the dual-cure modes to ensure long-term color-stability.

Light curing resin cements containing iodonium salts promote suitable apical bonding of posts to radicular dentin

Abstract The aim of this study was to analyze the efficiency of experimental light-curing resin cements (ERCs) with a ternary photo-initiator system containing diphenyliodonium hexafluorphosphate (DPI) and different amines on retention of glass-fiber posts to dentin (GFP). ERCs formulations: a 1:1 mass ratio of 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenylpropane and triethyleneglycol dimethacrylate. Camphorquinone was used as initiator. Six experimental groups were established according to the amine used: [ethyl-4-(dimethylamino)benzoate-EDMAB or 2-(dimethylamino)ethyl methacrylate-DMAEMA] and the concentration of DPI (0, 0.5 mol%, 1 mol%). The resin cements Variolink II (dual- and light-cured versions) were used as commercial reference. Eighty recently extracted bovine incisors (n = 10) were selected for this study. The roots were prepared and the fiber posts were cemented with the resin cement specified for each experimental group. Specimens from coronal, middle, and apical thirds of the root were subjected to push-out bond strength test 24 hours after bonding. Data were subjected to split-plot ANOVA and the Tukey test (p = 0.05). ERCs containing DPI showed statistically significant higher bond strengths compared with ERCs without DPI. ERCs containing DPI were statistically similar to VARIOLINK II - dual-cured and superior to VARIOLINK II - light-cured (except for EDMAB - 1DPI in the medium third and DMAEMA - 1DPI in the coronal third). Different amines did not influence post retention. The apical root region showed the lowest bond strength for the groups EDAB-0DPI, DMAEMA-0DPI and VARIOLINK II light-cured. Light-cured ERCs containing DPI were efficient for GFP retention to radicular dentin, with similar behaviour to that of dual-curing commercial resin cement.